Covalently closed microemulsions in presence of triblock terpolymers

发布时间:2009-05-04   点击次数:675次

Abstract:
This paper is focused on the influence of polystyrene (PS)–poly(1,4-butadiene) (PB)–poly(ethylene oxide) (PEO) triblock terpolymers on the w/o microemulsion of the pseudo-ternary system water/sodium dodecylsulfate (SDS)/xylene-pentanol. Despite the insolubility of the copolymer in
water as well as in the xylene–pentanol mixture, it can be incorporated into the w/o microemulsion and interactions between the triblock terpolymer molecules and the anionic surfactant headgroups can be detected by differential scanning calorimetry (DSC) measurements. Furthermore, dynamic
light scattering measurements were used to determine the aggregate diameter of the modified microemulsions. For lower polymer concentrations large aggregates between 100 and 500 nm can be observed. Surprisingly, at a higher terpolymer concentration of 5 wt%, significant smaller
aggregate diameters can be identified by dynamic light scattering and Cryo-SEM. One can conclude that the copolymers are incorporated in the inverse microemulsion droplets, where the PB blocks cover the water droplets. The thermally induced radical cross-linking of the butadiene units in the presence of azobisisobutyronitrile (AIBN) leads then to covalently closed nanocapsules with an average size of 10 nm.
Keywords:Triblock terpolymer; Microemulsion; Nanocapsules


上一篇 : Thermophysical properties of 1-hexyl-3-methyl imidazolium based ionic liquids with tetrafluoroborate    下一篇 :  Effect of Permeability on Aqueous Biopolymer Interfaces in Spinning Drop Experiments

分享到:

返回列表

北京东方德菲仪器有限公司主营产品:在线接触角测量仪,德国接触角测量仪,进口接触角测量仪,国产接触角测量仪,接触角张力测量仪
版权所有 地址:海淀区紫竹院路69号兵器大厦1010室 网站地图
备件销售电话 Tel:010-68920257/75/76/77 传真 Fax:010-68729983 邮编:100089 电子邮箱 E-mail:mary_wang@edcc.com.cn
京ICP备05028011号-2 返回首页 管理登陆 技术支持:化工仪器网

联系人
在线客服
用心服务成就你我